Abstract
The loading–unloading hysteresis behavior of unidirectional HTS40/PA6 carbon/polyamide laminates under off-axis compression has been examined both experimentally and constitutively in the present study. Monotonic compressive tests are first performed on unidirectional laminates to identify the basic properties of off-axis deformation. Then, five cycles of compressive loading and unloading tests are carried out with a gradually increasing peak stress for each specimen, followed by testing to failure. Significant nonlinear unloading behavior is observed after the material has been loaded into the nonlinear deformation region, and apparent plastic strain is seen after full unloading. The reloading curve also exhibits nonlinearity and conduces to a slightly open hysteresis loop with unloading. An approach is developed to predict the nonlinear hysteresis behavior of unidirectional composites by assuming an anelastic strain component in the nonlinear compressive deformation. The assumption of anelastic strain is a modification of Sun–Chen’s one-parameter plasticity model that considers the nonlinear deformation completely as plastic strain from monotonic tests. The modified model has been validated by the off-axis loading–unloading test results on unidirectional laminates. Results verify that the model accurately captures not only the plastic strain but also the complex nonlinear hysteresis behavior in the observed off-axis loading–unloading stress–strain curves.
References
| 1. | Carlsson, LA, Adams, DF, Pipes, RB. Experimental characterization of advanced composite materials. Boca Raton, FL: CRC Press, 2014. Google Scholar |
| 2. | Aboudi, J. Micromechanical analysis of composites by the method of cells. Appl Mech Rev 1989; 42: 193–221. Google Scholar | Crossref |
| 3. | Wang, J, Xiao, Y. Some improvements on Sun–Chen’s one-parameter plasticity model for fibrous composites – part I: constitutive modelling for tension–compression asymmetry response. J Compos Mater 2017; 51: 405–418. Google Scholar | SAGE Journals | ISI |
| 4. | Wang, J, Xiao, Y. Some improvements on Sun–Chen's one-parameter plasticity model for fibrous composites (Part II: finite element method implementation and applications). J Compos Mater 2017; 51: 533–545. Google Scholar | SAGE Journals | ISI |
| 5. | Surrel, Y, Vautrin, A. Plastic behaviour of fibrous laminae. Compos Sci Technol 1993; 49: 45–50. Google Scholar | Crossref | ISI |
| 6. | Ogi, K, Takeda, N. Effects of moisture content on nonlinear deformation behavior of CF/epoxy composites. J Compos Mater 1997; 31: 530–551. Google Scholar | SAGE Journals | ISI |
| 7. | Kim, W, Sun, CT. Modeling relaxation of a polymeric composite during loading and unloading. J Compos Mater 2002; 36: 745–755. Google Scholar | SAGE Journals | ISI |
| 8. | Espinosa, HD, Lu, HC, Zavattieri, PD. A 3-D finite deformation anisotropic visco-plasticity model for fiber composites. J Compos Mater 2001; 35: 369–410. Google Scholar | SAGE Journals | ISI |
| 9. | Kawai, M, Masuko, Y, Kawase, Y. Micromechanical analysis of the off-axis rate-dependent inelastic behavior of unidirectional AS4/PEEK at high temperature. Int J Mech Sci 2001; 43: 2069–2090. Google Scholar | Crossref | ISI |
| 10. | Ogasawara, T, Yokozeki, T, Onta, K. Linear and nonlinear torsional behavior of unidirectional CFRP and GFRP. Compos Sci Technol. 2007; 67: 3457–3464. Google Scholar | Crossref | ISI |
| 11. | Lemaitre, J, Chaboche, JL. Mechanics of solid materials. Cambridge University Press, 1994. Google Scholar |
| 12. | Sun, L, Wagoner, RH. Complex unloading behavior: nature of the deformation and its consistent constitutive representation. Int J Plast 2011; 27: 1126–1144. Google Scholar | Crossref | ISI |
| 13. | Lee, JY, Lee, JW, Lee, MG. An application of homogeneous anisotropic hardening to springback prediction in pre-strained U-draw/bending. Int J Solids Struct 2012; 49: 3562–3572. Google Scholar | Crossref | ISI |
| 14. | Mann, GE, Sumitomo, T, Cáceres, CH. Reversible plastic strain during cyclic loading–unloading of Mg and Mg–Zn alloys. Mater Sci Eng A. 2007; 456: 138–146. Google Scholar | Crossref | ISI |
| 15. | Min, J, Lin, J. Anelastic behavior and phenomenological modeling of Mg ZEK100-O alloy sheet under cyclic tensile loading–unloading. Mater Sci Eng A 2013; 561: 174–182. Google Scholar | Crossref | ISI |
| 16. | Sakai, J, Kawashima, K. Unloading and reloading stress–strain model for confined concrete. J Struct Eng 2006; 132: 112–122. Google Scholar | Crossref | ISI |
| 17. | Lam, L, Teng, JG. Stress–strain model for FRP-confined concrete under cyclic axial compression. Eng Struct 2009; 31: 308–321. Google Scholar | Crossref | ISI |
| 18. | Murakami, S, Mizobe, T. An inelastic constitutive equation of fiber reinforced plastic laminates. J Eng Mater Technol 1998; 120: 13–18. Google Scholar | Crossref | ISI |
| 19. | Ishii, T, Mizobe, T, Mizuno, M. Inelastic constitutive equation of polymer-matrix composites by taking into account transient recovery surface. J Soc Mater Sci 2001; 50: 973–979. (In Japanese). Google Scholar | Crossref |
| 20. | Chung, K, Ryou, H. Development of viscoelastic/rate-sensitive-plastic constitutive law for fiber-reinforced composites and its applications. Part I: theory and material characterization. Compos Sci Technol 2009; 69: 284–291. Google Scholar | Crossref | ISI |
| 21. | Drozdov, AD. Cyclic thermo-viscoplasticity of high density polyethylene. Int J Solids Struct 2010; 47: 1592–1602. Google Scholar | Crossref | ISI |
| 22. | Malinin, NN, Khadjinsky, GM. Theory of creep with anisotropic hardening. Int J Mech Sci 1972; 14: 235–246. Google Scholar | Crossref | ISI |
| 23. | Frederick, CO, Armstrong, PJ. A mathematical representation of the multiaxial Bauschinger effect. Mater High Temp 2007; 24: 1–26. Google Scholar | Crossref | ISI |
| 24. | Hahn, HT, Tsai, SW. Nonlinear elastic behavior of unidirectional composite laminae. J Compos Mater 1973; 7: 102–118. Google Scholar | SAGE Journals | ISI |
| 25. | Sun, CT, Chen, JL. A simple flow rule for characterizing nonlinear behavior of fiber composites. J Compos Mater 1989; 23: 1009–1020. Google Scholar | SAGE Journals | ISI |
| 26. | Ladeveze, P, LeDantec, E. Damage modelling of the elementary ply for laminated composites. Compos Sci Technol 1992; 43: 257–267. Google Scholar | Crossref | ISI |
| 27. | Hayakawa, K, Murakami, S, Liu, Y. An irreversible thermodynamics theory for elastic-plastic-damage materials. Eur J Mech A / Solids 1998; 17: 13–32. Google Scholar | Crossref | ISI |
| 28. | Barbero, EJ, Lonetti, P. An inelastic damage model for fiber reinforced laminates. J Compos Mater 2002; 36: 941–962. Google Scholar | SAGE Journals | ISI |
| 29. | ASTM D3410/D3410M-03 . Standard test method for compressive properties of polymer matrix composite materials with unsupported gage section by shear loading. West Conshohocken, PA: ASTM International, 2008. Google Scholar |
| 30. | Kawai, M, Saito, S. Off-axis strength differential effects in unidirectional carbon/epoxy laminates at different strain rates and predictions of associated failure envelopes. Compos Part A 2009; 40: 1632–1649. Google Scholar | Crossref | ISI |
| 31. | Cho, J, Fenner, J, Werner, B. A constitutive model for fiber-reinforced polymer composites. J Compos Mater 2010; 44: 3133–3150. Google Scholar | SAGE Journals | ISI |
| 32. | Xiao, Y, Kawai, M, Hatta, H. An integrated method for off-axis tension and compression testing of unidirectional composites. J Compos Mater 2011; 45: 657–669. Google Scholar | SAGE Journals | ISI |
| 33. | Kenaga, D, Doyle, JF, Sun, CT. The characterization of boron/aluminum composite in the nonlinear range as an orthotropic elastic-plastic material. J Compos Mater 1987; 21: 516–531. Google Scholar | SAGE Journals | ISI |
| 34. | Li, LB, Song, YD, Sun, YC. Modeling loading/unloading hysteresis behavior of unidirectional C/SiC ceramic matrix composites. Appl Compos Mater 2013; 20: 655–672. Google Scholar | Crossref | ISI |
| 35. | Ahn, BK, Curtin, WA. Strain and hysteresis by stochastic matrix cracking in ceramic matrix composites. J Mech Phys Solids 1997; 45: 177–209. Google Scholar | Crossref | ISI |
| 36. | Wang, J, Guo, Q, Xiao, Y. An optimal method for the determination of parameter in Sun and Chen’s one-parameter plasticity model. CCCM-2, Zhenjiang, 2015. Google Scholar |
| 37. | Wang, J, Xiao, Y, Kawai, M. Parameter identification problem in one-parameter plasticity model for fibrous composites. Adv Compos Mater. Submitted for publication. Google Scholar |